| Title: | High temperature corrosion of 310S austenitic stainless steel in CO2/HCl environment |
| Authors: | Pornpibunsompop, Tosapolporn
Thanakijkasem, Purit |
| Keywords: | High temperature corrosion
austenitic stainless steel |
| Issue Date: | 2015 |
| Publisher: | Defence Technology Institute |
| Series/Report no.: | 58018; |
| Abstract: | High temperature corrosion of SUS 310S
austenitic stainless steel was investigated comparatively in
CO2 and HCl/H2O environment at 900⁰C. The thickness of
corrosion layer in case of CO2 surrounding was thinner than
HCl/H2O environment because of protective chromium oxide
layer formation. The corrosion layer of HCl/H2O environment
was porous and weak caused by water vapor leading to
intergranular corrosion and intermetallic compounds (oxide,
chloride, carbide) |
| Description: | บทความวิจัย |
| URI: | http://hdl.handle.net/123456789/1911 |
| Appears in Collections: | ผลงานด้านการวิจัยและพัฒนานวัตกรรมและเทคโนโลยีป้องกันประเทศเพื่อนำไปสู่อุตสาหกรรมป้องกันประเทศ
|
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.
|